TPU Berbasis Polikarbonat Tahan Minyak dan Hidrolisis Seri C
Fitur
Ketahanan Penuaan Yang Sangat Baik, Ketahanan Minyak, Ketahanan Hidrolisis, Ketahanan Suhu Tinggi, Ketahanan UV, Sifat Fisik Yang Sangat Baik & Ketahanan Pelapukan.
Aplikasi
Selang & Tabung, Film & Lembaran, Selang Pemadam Kebakaran, Selang Lay-Flat untuk Frac Minyak Serpih, Tangki Minyak, dll.
| Properti | Standar | Satuan | Bab 80 | Bab 85 | Bab 90 | Bab 95 |
| Kepadatan | ASTM D792 | gram/cm3 | 1.15 | 1.15 | 1.15 | 1.15 |
| Kekerasan | ASTM D2240 | Pantai A/D | 82/- | 85/- | 90/- | 95/- |
| Kekuatan Tarik | ASTM D412 | MPa | 25 | 30 | 35 | 45 |
| Modulus 100%. | ASTM D412 | MPa | 7 | 8 | 12 | 20 |
| Modulus 300%. | ASTM D412 | MPa | 14 | 20 | 30 | 40 |
| Perpanjangan Saat Istirahat | ASTM D412 | ％ | 550 | 500 | 400 | 350 |
| Kekuatan Robek | ASTM D624 | kN/m | 90 | 120 | 140 | 180 |
| Kerugian Abrasi DIN | DIN 53516 | mm3 | 25 | 25 | 25 | 25 |
| Tg | DSC | ℃ | -30 | -20 | -15 | -8 |
CATATAN: Nilai di atas ditampilkan sebagai nilai tipikal dan tidak boleh digunakan sebagai spesifikasi.
Panduan Pemrosesan
Untuk hasil optimal, sebelumnya dilakukan pengeringan produk selama 3-4 jam pada suhu tertentu dalam TDS.
Produk dapat digunakan untuk cetakan injeksi atau ekstrusi, dan silakan periksa detail lebih lanjut di TDS.
| Panduan Pemrosesan Cetakan Injeksi | Panduan Pemrosesan untuk Ekstrusi | |||
| Barang | Parameter | Barang | Parameter | |
| Nozel (℃) | Diberikan dalam TDS | Mati (℃) | Diberikan dalam TDS | |
| Zona Pengukuran (℃) | Adaptor (℃) | |||
| Zona Kompresi (℃) | Zona Pengukuran (℃) | |||
| Zona Makan (℃) | Zona Kompresi (℃) | |||
| Tekanan Injeksi (bar) | Zona Makan (℃) | |||
Inspeksi
Semua produk diperiksa dengan baik selama produksi dan setelah produksi. Certificate of Analysis (COA) dapat diberikan bersama dengan produk.
Kemasan
25KG/bag, 1250KG/pallet atau 1500KG/pallet, palet kayu olahan