C Mfululizo wa Upinzani wa Mafuta na Upinzani wa Hydrolysis ya Polycarbonate-Based TPU
Vipengele
Ustahimilivu Bora wa Kuzeeka, Ustahimilivu wa Mafuta, Ustahimilivu wa Haidrolisisi, Ustahimilivu wa Halijoto ya Juu, Upinzani wa UV, Sifa Bora za Kimwili&Upinzani wa Hali ya Hewa.
Maombi
Hose&Tube, Filamu na Karatasi, Hose ya Moto, Hose ya Lay-Flat kwa Frac ya Mafuta ya Shale, Tangi la Mafuta, n.k.
| Mali | Kawaida | Kitengo | C80 | C85 | C90 | C95 |
| Msongamano | ASTM D792 | g/cm3 | 1. 15 | 1. 15 | 1. 15 | 1. 15 |
| Ugumu | ASTM D2240 | Pwani A/D | 82/- | 85/- | 90/- | 95/- |
| Nguvu ya Mkazo | ASTM D412 | MPa | 25 | 30 | 35 | 45 |
| 100% Moduli | ASTM D412 | MPa | 7 | 8 | 12 | 20 |
| 300% Moduli | ASTM D412 | MPa | 14 | 20 | 30 | 40 |
| Kuinua wakati wa Mapumziko | ASTM D412 | ％ | 550 | 500 | 400 | 350 |
| Nguvu ya machozi | ASTM D624 | kN/m | 90 | 120 | 140 | 180 |
| Kupoteza kwa Abrasion ya DIN | DIN 53516 | mm3 | 25 | 25 | 25 | 25 |
| Tg | DSC | ℃ | -30 | -20 | -15 | -8 |
KUMBUKA: Thamani zilizo hapo juu zinaonyeshwa kama thamani za kawaida na hazifai kutumika kama vipimo.
Mwongozo wa Uchakataji
Kwa matokeo bora, kukausha hapo awali kwa bidhaa wakati wa masaa 3-4 kwa joto fulani katika TDS.
Bidhaa zinaweza kutumika kwa ukingo wa sindano au extrusion, na tafadhali angalia maelezo zaidi katika TDS.
| Mwongozo wa Usindikaji wa Ukingo wa Sindano | Mwongozo wa Uchakataji kwa Uchimbaji | |||
| Kipengee | Kigezo | Kipengee | Kigezo | |
| Pua(℃) | Imetolewa katika TDS | Kufa (℃) | Imetolewa katika TDS | |
| Eneo la Kupima mita(℃) | Adapta(℃) | |||
| Eneo la Mfinyazo(℃) | Eneo la Kupima mita (℃) | |||
| Eneo la Kulisha(℃) | Eneo la Mfinyazo (℃) | |||
| Shinikizo la sindano (bar) | Eneo la Kulisha (℃) | |||
Ukaguzi
Bidhaa zote hukaguliwa vizuri wakati wa uzalishaji na baada ya uzalishaji.Cheti cha Uchambuzi (COA) kinaweza kutolewa pamoja na bidhaa.
Ufungaji
25KG/begi, 1250KG/pallet au 1500KG/pallet, godoro la mbao lililochakatwa